Continuous casting and rolling steel billet temperature raising and temperature compensation induction heating furnace

Technical

Equipment technical information

Continuous casting and rolling steel billet temperature raising and temperature compensation induction heating furnace

Time: 2021-08-05

At present, some steel mills at home and abroad have adopted the continuous steel casting process. The surface temperature of the continuous casting billet after leaving the continuous casting machine is sent to the rolling mill. Rolling is not possible, so the continuous casting billet must be cut and stacked, or placed in a uniform temperature furnace to continue heating. For such a continuous casting slab, the average temperature is about 925°C. If supplementary heating is performed on the production line, the continuous casting slab can be rolled from 925°C to 1250°C. Since the surface temperature of the continuous casting slab is low and the temperature of the center part is relatively high, and induction heating is first heated from the surface and the heat is transferred to the center, the continuous casting slab is heated by induction heating for supplementary heating and then continues to be rolled, which is a good way to save energy. The method makes full use of the waste heat of the blank, and many steel plants abroad have already implemented this process.

The heat required for continuous casting billet heating from 925°C to 1250^ is equivalent to 60kW • h/°C. If the induction heating efficiency is 50%, its unit power consumption is 120kW • h/°C, which can save energy by 68%. Figure 1-3 shows the appearance of the continuous casting billet induction heating furnace. The number of inductors is determined by the production rate of the continuous casting billet. In order to support the continuous casting slab, water-cooled spokes are arranged between the inductors, and the continuous casting slab is conveyed through each of the inductors to be heated to the required rolling temperature.